70℃热塑性低烟无卤阻燃绝缘料 EJW70,EJW70C,EJW70A
70℃Thermoplastic Low-smoke Halogen-free Flame-retardant Insulation Compound ...
型号:0

参考价:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Description and Application  产品描述和用途
EJW70,EJW70C,EJW70A are thermoplastic low-smoke halogen-free flame-retardant insulation compounds, which don’t contain any heavy metal like Pb, Ba, Cd, Cr, Sn and Sb. The properties can meet RoHS Standard. They have excellent mechanical and flame-retardant properties with temperature resistant from -40℃to 70℃. They are mainly used for the insulation of communication cables, control cables and power cables.
EJW70,EJW70C,EJW70A是热塑性低烟无卤绝缘料。不含Pb、Ba、Cd、Cr、Sn、Sb六大重金属。具有优异的物理机械性能和阻燃性能,可耐温-40℃~70℃,其性能均能满足RoHS的标准要求。主要用于通信电缆,控制电缆和电力电缆的绝缘层。
 
Processing Indicator   加工工艺
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低烟无卤专用螺杆,长径比L/D=20-25。
Model
牌号
Machine Barrel Temperature
机筒温度
Molding Temprature
机头温度
EJW70/EJW70C/EJW70A 130-140℃ 150-160℃
 
 
Physical and Electrical Properties   物理及电性能指标
Item
试验项目
Unit
单位
Specification
技术要求
EJW70 EJW70C EJW70A
Density
密度
g/cm3 ≤1.5 ≤1.5 ≤1.55
Tensile Strength
拉伸强度
MPa ≥10 ≥10 ≥10
Elongation at Break
断裂伸长率
% ≥150 ≥150 ≥150
Aging Conditions
热老化条件
/ 100℃×168h
Tensile Strength Variation
拉伸强度变化率
% ±25 ±25 ±25
Elongation Variation
断裂伸长率变化率
% ±25 ±25 ±25
Thermal
Deformation
热变形
Condition 70℃×6h
Variation % ≤50 ≤50 ≤50
Dielectric Strength
介电强度
MV/m ≥20 ≥20 ≥20
Brittle Temperature With Low Temperature Impact
低温冲击脆化温度
-40 -40 -40
20℃Volume Resistivity
20℃体积电阻率
Ω.m ≥1.0×1012
Water Absorption吸水性实验
14 days at 70℃
mg/cm2 ≤5 ≤5 ≤5
Oxygen Index
氧指数
% ≥32 ≥36 ≥38
HCLGas Evolution
HCL气体发生量
Mg/g ≤1.0 ≤1.0 ≤1.0
PH Value
PH值
/ ≥4.3 ≥4.3 ≥4.3
Smoke Density烟密度
– No-flame Mode无焰模式
– Flame Mode有焰模式
Ds max  
≤200
≤100
 
≤200
≤100
 
≤200
≤100
Conductivity
电导率
uS/mm ≤10 ≤10 ≤10
Toxicity Index
毒性指数
/ ≤5.0 ≤5.0  ≤5.0
 
 
Attentions 注意事项:
1)The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘干后才能使用,材料一经开封,建议12小时之内用完。
2)Please ensure the screw, barrel , hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前确保螺杆、机筒、加料斗彻底清理干净,加工过程中严禁带入杂质。
3)If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速挤出时,请慢慢逐渐加快螺杆转速,以免塑化不良,电缆表面毛糙。